Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.41 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 10 g/10min |
| Water absorption rate | | ISO 62 | 0.65 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 144 MPa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Yield | ISO 527-2/50 | 9.0 % |
| Flexural modulus | | ISO 178 | 2700 MPa |
| bending strength | | ISO 178 | 67.0 MPa |
| Tensile modulus | | ISO 527-2 | 2800 MPa |
| tensile strength | Yield | ISO 527-2/50 | 32.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 5.5 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 5.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 35 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 104 °C |
| melting temperature | | ISO 3146 | 166 °C |
| Linear coefficient of thermal expansion | | DIN 52328 | 1.2E-04 cm/cm/°C |
| vicat | | ISO 306/B50 | 151 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.