Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.00 -- |
| Water absorption rate | | % | 1.4 -- |
| Water absorption rate | | % | 0.70 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | MPa | 25.0 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Nominal tensile fracture strain | | % | >50 -- |
| Tensile modulus | | MPa | 300 250 |
| tensile strength | Yield | MPa | 20.0 -- |
| tensile strength | Break | MPa | 45.0 30.0 |
| Tensile strain | Yield | % | 45 -- |
| Tensile strain | Break | % | >50 -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 12 13 |
| Charpy Notched Impact Strength | | | 无断裂 |
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | -- 1E+13 |
| dielectric strength | | kV/mm | 32 -- |
| Compared to the Leakage Tracking Index (CTI) | | V | -- |
| Surface Resistivity | | ohms | -- 1E+12 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 50.0 -- |
| Heat distortion temperature | | °C | 40.0 -- |
| Continuous use temperature | | °C | 80.0 -- |
| Continuous use temperature | | °C | 110 -- |
| melting temperature | | °C | 173 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.