PA6 BKV140H2.0 900051 LANXESS GERMANY

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			抗冲击热稳定性
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	100	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	110	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	90	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	90	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638/ISO 527	11200	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	174	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	10400	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	280	kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	FlexuralStrainatFlexuralStrength5(23°C)		4.2	%
Tensile modulus	23°C	ISO 527-2/1	12000	Mpa
tensile strength	Break,23°C	ISO 527-2/5	185	Mpa
Tensile strain	Break,23°C	ISO 527-2/5	3.4	%
Bending modulus	23°C	ISO 178/A	11000	Mpa
bending strength	3.5%Strain	ISO 178/A	280	Mpa
bending strength	bending strength	23°C	ISO 178	290	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	HB
Vicat softening temperature		ASTM D1525/ISO R306	200	℃（℉）
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	217	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	201	°C
Melting temperature		ISO 11357-3	220	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.46
Shrinkage rate	TD:280°C,2.00mm2	ISO 294-4	0.75	%
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.090	%
		Shrinkage rate	MD:280°C,2.00mm2	ISO 294-4	0.21	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.070	%
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut		ISO 1874	PA6HI.GR.14-120.GF40

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.