LDPE 21F430
0
- Properties:Good printing adaptabilitygood precipitationhomopolymer
- Usages:Handbagsmovie applications
CompareTechnical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D-2457 | 50 | |
| Haze ratio | ASTM D-1003 | 12 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183/D | 0.923 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 0.8 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile elongation at break (TD) | ISO 1184 | 500 % | |
| Falling hammer impact | ASTM D-1709A | 140 g | |
| ASTM D-1894 | ＞0.5 | ||
| Film thickness - Tested | um | 50 | |
| Secant modulus | ISO 1184 | 230 MPa | |
| ISO 1184 | 215 MPa | ||
| Tensile yield stress (MD) | ISO 1184 | 11 MPa | |
| Tensile yield stress (TD) | ISO 1184 | 11 MPa | |
| Tensile modulus (MD) | ISO 1184 | 21 MPa | |
| Tensile modulus (TD) | ISO 1184 | 20 MPa | |
| Tensile elongation at break (MD) | ISO 1184 | 150 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/A | 94 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.