Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.60 % |
| Water absorption rate | | ASTM D570 | 0.30 % |
| Water absorption rate | | ASTM D570 | 0.70 % |
| density | | ASTM D792 | 1.04 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.60 % |
| melt mass-flow rate | | ASTM D1238 | 15 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 95 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 160 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 70.0 MPa |
| Flexural modulus | | ASTM D790 | 2100 MPa |
| elongation | Break | ASTM D638 | 15 % |
| tensile strength | | ASTM D638 | 35.0 MPa |
| Tensile modulus | | ASTM D638 | 2000 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTM D495 | PLC 5 |
| arc resistance | | ASTM D495 | 160 sec |
| dielectric strength | | ASTM D149 | 18 kV/mm |
| Hot wire ignition (HWI) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | | UL 746 | PLC 3 sec |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 0 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Imp | | UL 746 | 60.0 °C |
| RTI Elec | | UL 746 | 60.0 °C |
| vicat | | ASTM D1525 | 105 °C |
| Heat distortion temperature | | ASTM D648 | 92.0 °C |
| Heat distortion temperature | | ASTM D648 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare