PC 201-22 STYRON US

Form：Granules | Grade：Injection grade

Properties:

High mobility

Typical Applications:

Food containers

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Food containers
Properties:	High mobility

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.586
Refractive index	Refractive index		ISO 489	1.586
transmissivity		ASTM D1003	89.0	%
turbidity		ASTM D1003	1.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap		ASTM D1822	378	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA2	70.0	kJ/m²
	Charpy Notched Impact Strength	-30°C	ISO 179/1eA2	11.0	kJ/m²
		Charpy Notched Impact Strength	23°C	ISO 179/1eU2	NoBreak
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eU2	NoBreak
Impact strength of cantilever beam gap	23°C	ASTM D256	750	J/m
	Impact strength of cantilever beam gap	23°C	ISO 180/A	74	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	NoBreak
Suspended wall beam without notch impact strength	23°C	ISO 180	NoBreak
InstrumentedDartImpact	23°C,TotalEnergy	ASTM D3763	72.3	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
BurningBehav.at1.6mmnom.thickn	1.60mm,UL	ISO 12102	HB
Burning Behav.atthicknessh	3.20mm,UL	ISO 12102	HB
Extreme Oxygen Index		ISO 4589-2	26	%
Limiting Oxygen Index (LOI)		ISO 4589-22	26	%
Average degree of combustion		ASTM D635	3	CM
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Taber abraser		ASTM D1044	45	%
tensile strength	Break	ASTM D638	65.5	Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	66.0	Mpa
Tensile strain	Yield	ISO 527-22	6.0	%
elongation	Break	ASTM D638	120	%
Tensile strain	Break	ISO 527-2/50	120	%
Nominal fracture strain		ISO 527-22	>50	%
Bending modulus		ASTM D790	2410	Mpa
Bending modulus	Bending modulus		ISO 178	2400	Mpa
bending strength		ASTM D790	96.5	Mpa
bending strength	bending strength		ISO 178	97.0	Mpa
Tensile modulus		ASTM D638	2340	Mpa
	Tensile modulus		ISO 527-2/50	2300	Mpa
	Tensile modulus	Tensile modulus		ISO 527-22	2300	Mpa
tensile strength	Yield	ASTM D638	60.0	Mpa
	tensile strength	Yield	ISO 527-2/50	60.0	Mpa
	tensile strength	tensile strength	Yield	ISO 527-22	60.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	139	°C
	Hot deformation temperature	0.45MPa,Annealed	ASTM D648	142	°C
		Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	142	°C
			Hot deformation temperature	0.45MPa	ISO 75-22	142	°C
				Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	126	°C
					Hot deformation temperature	1.8MPa,Annealed	ASTM D648	139	°C
						Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	126	°C
						Hot deformation temperature	Hot deformation temperature	1.8MPa	ISO 75-22	128	°C
Vicat softening temperature		ASTM D15257	147	°C
	Vicat softening temperature		ISO 306/B50	147	°C
	Vicat softening temperature	Vicat softening temperature	50N	ISO 3062	147	°C
Ball pressure temperature		IEC 60335-1	125	°C
Linear coefficient of thermal expansion	MD：-40to82°C	ASTM D696	6.8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-22	7E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.20	g/cm³
	density		ISO 1183/A	1.20	g/cm³
	density	density		ISO 11832	1200	kg/m3
melt mass-flow rate	300°C/1.2kg	ASTM D1238	22	g/10min
melt mass-flow rate	melt mass-flow rate	300°C/1.2kg	ISO 1133	22	g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 11332	18.0	cm3/10min
Shrinkage rate	MD	ASTM D955	0.50-0.70	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.50-0.70	%
Water absorption rate	23°C,24hr	ASTM D570	0.15	%
	Water absorption rate	23°C,24hr	ISO 62	0.15	%
		Water absorption rate	Equilibrium,23°C,50%RH	ASTM D570	0.32	%
		Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.32	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		IEC 60243-1	17	KV/mm
Dielectric strength	Dielectric strength		IEC 60243-12	17	KV/mm
Dielectric constant	60Hz	ASTM D150	3.00
Dielectric constant	Dielectric constant	1MHz	ASTM D150	3.00
Relative permittivity	100Hz	IEC 602502	3.00
Relative permittivity	Relative permittivity	1MHz	IEC 602502	3.00
Dissipation factor	50Hz	ASTM D150	1E-03
	Dissipation factor	1MHz	ASTM D150	2E-03
		Dissipation factor	100Hz	IEC 602502	1E-03
		Dissipation factor	Dissipation factor	1MHz	IEC 602502	2E-03
Compared to the anti leakage trace index	2.00mm,SolutionA	IEC 60112	PLC 2
Volume resistivity		ASTM D257	2E+17	ohms·cm
Volume resistivity	Volume resistivity		IEC 600932	>1.0E+13	ohms·m
Dielectric strength		ASTM D149	17	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ASTM D785	72
Rockwell hardness	Rockwell hardness	R-Sale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.