MVLDPE FPS117-C NOVA CANADA

Form：Granules | Grade：Thin film grade

Properties:

antioxidantGood sealing performanceHigh toughnessEasy to process

Typical Applications:

filmLaminatefilm

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	film \| Laminate \| film
Properties:	antioxidant \| Good sealing performance \| High toughness \| Easy to process

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity	25.0μm,BlownFilm2	ASTM D1003	7.0	%
turbidity	turbidity	25.0μm,BlownFilm3	ASTM D1003	16	%
gloss	45°,25.0μm,BlownFilm2	ASTM D2457	72
gloss	gloss	45°,25.0μm,BlownFilm3	ASTM D2457	37
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190°C/2.16kg	ASTM D1238	1.0	g/10min
film	Test Condition	Test Method	Test Result	Test Unit
film thickness			25	µm
Secant modulus -1% Decant, MD	25μm,BlownFilm	ASTM D882	126	Mpa
Secant modulus -1% Decant, TD	25μm,BlownFilm	ASTM D882	132	Mpa
tensile strength	Yield,25μm,BlownFilm	ASTM D882	9.00	Mpa
	tensile strength	Yield,25μm,BlownFilm	ASTM D882	9.00	Mpa
		tensile strength	Break,25μm,BlownFilm	ASTM D882	46.0	Mpa
		tensile strength	tensile strength	Break,25μm,BlownFilm	ASTM D882	42.0	Mpa
Tensile strain	Break,25μm,BlownFilm，MD	ASTM D882	540	%
Tensile strain	Tensile strain	Break,25μm,BlownFilm	ASTM D882	760	%
Dart impact	25μm,Blown Film	ASTM D1709A	400	g
Elmendorf tear strength	25μm,BlownFilm，MD	ASTM D1922	300	g
Elmendorf tear strength	Elmendorf tear strength	25μm,BlownFilm，TD	ASTM D1922	450	g
Seal Initiation Temperature	25μm,BlownFilm		100	°C
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Low friction puncture	25.0μm，吹膜	Internal Method	790	J/cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.