Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.41 g/cm³ |
| Water absorption rate | | | 0.30 % |
| Water absorption rate | | | 0.14 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 102 |
| | ISO2039-1 | 325 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| Limiting Oxygen Index | | ISO4589-2 | 40 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO527-2 | 5.0 % |
| compression stress | | ISO604 | 97.0 MPa |
| compression stress | | ISO604 | 49.0 MPa |
| Tensile stress | | ISO527-2 | 130 MPa |
| Tensile modulus | | ISO527-2 | 7700 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 35 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | <1.0E+5 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 230 °C |
| melting temperature | | | 340 °C |
| | | 2.5E-05 cm/cm/°C |
| | | 2.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 0.92 W/m/K |
| maximum service temperature | | | 250 °C |
| maximum service temperature | | | 310 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.