Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 4.5to7.5 g/10min |
| Shrinkage rate | | | 0.40to0.60 % |
| Water absorption rate | Equilibrium | ASTM D570 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 110 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D523 | 60 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-1 | 650 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| styrene content | | 内部方法 | 0.050 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTM D638 | 43.0 MPa |
| elongation | Break | ASTM D638 | 45 % |
| Flexural modulus | | ASTM D790 | 2300 MPa |
| bending strength | Yield | ASTM D790 | 65.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | DIN 53453 | 12 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 12 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D15252 | 104 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 9E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.17 W/m/K |
| Heat distortion temperature | | ASTM D648 | 108 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.