Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.50 g/cm³ |
| Shrinkage rate | | ISO294-4,ISO2577 | 0.36 % |
| Water absorption rate | | ISO62 | 0.60 % |
| melt mass-flow rate | | ISO1133 | 10到15 g/10min |
| Shrinkage rate | | ISO294-4,ISO2577 | 0.61 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/A | 6.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 7300 MPa |
| Tensile stress | | ISO527-2 | 125 MPa |
| Tensile strain | Yield | ISO527-2 | 2.5 % |
| Flexural modulus | | ISO178 | 6800 MPa |
| Bending stress | | ISO178 | 150 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC60250 | 4.20 |
| Dissipation Factor | | IEC60250 | 2E-03 |
| Dissipation Factor | | IEC60250 | 0.010 |
| CTI | | IEC60112 | 125 V |
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 37 kV/mm |
| dielectric constant | | IEC60250 | 4.20 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/A | 220 °C |
| Glass Transition Temperature | | ISO11357-2,DSC | 225 °C |
| | ISO11359-2 | 2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.