| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.37 g/cm³ |
| Water absorption rate | | ASTM D570 | 14 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 67 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 61 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 110 MPa |
| tensile strength | Across Flow | ASTM D638 | 58.6 MPa |
| bending strength | | ASTM D790 | 154 MPa |
| bending strength | | ASTM D790 | 105 MPa |
| compressive strength | | ASTM D695 | 96.5 MPa |
| compressive strength | | ASTM D695 | 80.7 MPa |
| compressive strength | | ASTM D695 | >310 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 0 mm/min |
| Hot wire ignition (HWI) | | UL 746 | PLC 2 sec |
| dielectric strength | | ASTM D149 | 60000 V |
| dielectric strength | | ASTM D149 | 12 kV/mm |
| dielectric constant | | ASTM D150 | 6.81 |
| dielectric constant | | ASTM D150 | 5.93 |
| Dissipation Factor | | ASTM D150 | 0.054 |
| Dissipation Factor | | ASTM D150 | 0.052 |
| arc resistance | | ASTM D495 | 128 sec |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Elec | | UL 746 | 90.0 °C |
| RTI | | UL 746 | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.