Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792 | 1.11 g/cm³ |
melt mass-flow rate | | ASTM D1238 | 16 g/10min |
Shrinkage rate | | ASTM D955 | 0.60 % |
Water absorption rate | | ASTM D570 | 0.25 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | R-Scale | ASTM D785 | 115 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | HB |
Hot filament ignition temperature | | AS/NZS60695.2.12 | 550 °C |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Dart impact | | ASTM D3029 | 55.0 J |
Impact strength of cantilever beam gap | | ASTM D256 | 500 J/m |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | | ASTM D638 | 52.0 MPa |
elongation | | ASTM D638 | 120 % |
Flexural modulus | | ASTM D790 | 2400 MPa |
bending strength | | ASTM D790 | 84.0 MPa |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTM D648 | 96.0 °C |
Heat distortion temperature | | ASTM D648 | 99.0 °C |
Heat distortion temperature | | ASTM D648 | 105 °C |
vicat | | ASTM D15254 | 128 °C |
Linear coefficient of thermal expansion | | ASTM D696 | 7.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.