Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.20 g/cm³ |
| Shrinkage rate | | | 0.40to0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | 115 MPa |
| Tensile strain | Break | ISO 527-2 | 4.0 % |
| Flexural modulus | | ISO 178 | 4500 MPa |
| bending strength | | ISO 178 | 160 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 7.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| dielectric strength | | IEC 60243-1 | 22 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | >200 °C |
| Heat distortion temperature | | ISO 75-2/A | 190 °C |
| melting temperature | | ISO 3146 | 221 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.