PC EN-1052 K2261 Samsung Cheil South Korea

Form：Granules | Grade：Flame retardant grade

Properties:

Flame retardantLow temperature resistanc

Typical Applications:

AdapterMechanical accessories

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Adapter \| Mechanical accessories
Properties:	Flame retardant \| Low temperature resistanc

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	65	kJ/m²
	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	540	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	710	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	70	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	V-2
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break	ISO 527-2/50	110	%
elongation	Break	ASTM D638	94	%
tensile strength	Break	ISO 527-2/50	67.0	Mpa
	tensile strength	Break	ASTM D638	61.0	Mpa
		tensile strength	Yield	ASTM D638	52.0	Mpa
		tensile strength	tensile strength	Yield	ISO 527-2/50	55.0	Mpa
bending strength		ISO 178	80.0	Mpa
bending strength	bending strength		ASTM D790	75.0	Mpa
Bending modulus		ISO 178	2100	Mpa
Bending modulus	Bending modulus		ASTM D790	2100	Mpa
Tensile modulus		ASTM D638	1900	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/50	2100	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Str	1.5mm	UL 746	130	°C
RTI Imp	1.5mm	UL 746	130	°C
RTI Elec	1.5mm	UL 746	130	°C
Vicat softening temperature	--	ISO 306/B120	145	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	142	°C
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	123	°C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	121	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	129	°C
			Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	135	°C
			Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	135	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.18	g/cm³
density	density		ISO 1183	1.18	g/cm³
melt mass-flow rate	250°C/10.0kg	ASTM D1238	19	g/10min
melt mass-flow rate	melt mass-flow rate	250°C/10.0kg	ISO 1133	19	g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.54-0.66	%
	Shrinkage rate	TD：3.20mm	ASTM D955	0.56-0.69	%
		Shrinkage rate	TD:3.20mm	ISO 2577	0.56-0.69	%
		Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO 2577	0.54-0.66	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	120
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.