Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| SpiralFlow | | 内部方法 | 46.0 cm |
| Shrinkage rate | | 内部方法 | 1.0到1.4 % |
| density | | ISO1183 | 0.900 g/cm³ |
| melt mass-flow rate | | ISO1133 | 7.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 90 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Gardner glossiness | | ASTMD523 | 90 |
| Haze ratio | | ISO14782 | 25 % |
| Haze ratio | | ISO14782 | 60 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 1.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 1050 MPa |
| Tensile stress | Yield | ISO527-2 | 26.0 MPa |
| Nominal tensile fracture strain | | ISO527-2 | >400 % |
| Flexural modulus | | ISO178 | 1000 MPa |
| Bending stress | | ISO178 | 30.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 80.0 °C |
| vicat | | ISO306 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare