PA6 TS-V0 EMS-CHEMIE SWITZERLAND

178

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedThermal stability

Typical Applications:

Automotive Applications

Supplier(4)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications
Properties:	Glass fiber reinforced \| Thermal stability

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	干燥｜35
Flammability level		UL 94	干燥｜V-0
Flammability level	Flammability level		UL 94	干燥｜V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	干燥｜3.0	kJ/m²
	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	调节后｜3.0	kJ/m²
		Charpy Notched Impact Strength	23°C	ISO 179/1eA	干燥｜4.0	kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	调节后｜15	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	干燥｜70	kJ/m²
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	调节后｜-	kJ/m²
		Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	干燥｜75	kJ/m²
		Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	调节后｜100	kJ/m²
Tensile modulus		ISO 527-2	干燥｜3600	Mpa
Tensile modulus	Tensile modulus		ISO 527-2	调节后｜1600	Mpa
tensile strength	Yield		干燥｜85	Mpa
	tensile strength	Yield		调节后｜50	Mpa
		tensile strength	Break	ISO 527-2	干燥｜75	Mpa
		tensile strength	tensile strength	Break	ISO 527-2	调节后｜50	Mpa
Tensile strain	Break	ISO 527-2	干燥｜4.0	%
Tensile strain	Tensile strain	Break	ISO 527-2	调节后｜15	%
Nominal tensile fracture strain		ISO 527-2	干燥｜10	%
Nominal tensile fracture strain	Nominal tensile fracture strain		ISO 527-2	调节后｜＞50	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 11357-3	干燥｜260	°C
Continuous use temperature	--4	Internal Method	干燥｜200	°C
Continuous use temperature	Continuous use temperature	--3	ISO 2578	干燥｜100 -120	°C
Linear coefficient of thermal expansion	TD	ISO 11359-2	干燥｜9.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	干燥｜7.0E-5	cm/cm/°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/A	干燥｜210	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/C	干燥｜70	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	干燥｜2.5	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	干燥｜8.0	%
Shrinkage rate	MD	ISO 294-4	干燥｜0.70	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	干燥｜0.80	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1 MHz		调节后｜0.070
	Dissipation factor	1 MHz		干燥｜0.015
		Dissipation factor	100 Hz		调节后｜0.15
		Dissipation factor	Dissipation factor	100 Hz		干燥｜5.0E-3
Relative permittivity	1 MHz		调节后｜4.00
	Relative permittivity	1 MHz		干燥｜3.00
		Relative permittivity	100 Hz		调节后｜8.00
		Relative permittivity	Relative permittivity	100 Hz		干燥｜3.00
Dielectric strength		IEC 60243-1	调节后｜26	KV/mm
Dielectric strength	Dielectric strength		IEC 60243-1	干燥｜28	KV/mm
Volume resistivity		IEC 60093	调节后｜1.0E+11	ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	干燥｜1.0E+13	ohms·cm
Surface resistivity		IEC 60093	调节后｜1.0E+10	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA6 TS-V0 EMS-CHEMIE SWITZERLAND

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index