Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | BS903 | 1.26 g/cm³ |
| Shrinkage rate | | | 0.40 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| stripping time | | | 480 min |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| | | 19 Pa·s |
| | | 25 Pa·s |
| Pot Life | | 75 min |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Supporting hardness | | ASTMD2240 | 22 |
| Tensile modulus | | BS903 | 0.930 MPa |
| Tensile modulus | | | 1.50 MPa |
| tensile strength | | BS903 | 3.64 MPa |
| elongation | Break | BS903 | 500 % |
| tear strength | | BS903 | 26.2 kN/m |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| VolumetricExpansion | | | 7.4E-04 cm/cm/°C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | | 2.5E-04 cm/cm/°C |
| Service | | | -50到200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.