Copolyester 0113 Eastman Chemical Company

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-40°C	ASTM D256	37	J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	100	J/m
		Impact strength of cantilever beam gap	-40°C3	ISO 180	4.2	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C3	ISO 180	6.2	kJ/m²
Suspended wall beam without notch impact strength	-40°C	ASTM D4812	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	无断裂
Multi axis Instrumented Impact Energy	-40°C,能量to力量峰值	ISO 6603-2	13.0	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C,能量to力量峰值	ISO 6603-2	12.0	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break,23°C,4.00mm	ISO 527-2	60	%
Bending modulus	23°C	ASTM D790	2100	MPa
Bending modulus	Bending modulus	23°C,4.00mm	ISO 178	2000	MPa
bending strength	23°C,4.00mm	ISO 178	68.0	MPa
bending strength	bending strength	Yield,23°C	ASTM D790	70.0	MPa
tear strength	10%solids&6/9AFNewtestsolution:23°C		1.0to2.0	%
tear strength	tear strength	10%solids&6/9AFtestoil:23°C		1.0to2.0	%
elongation	Break,23°C	ASTM D638	110	%
tensile strength	Yield,23°C,4.00mm	ISO 527-2	50.0	MPa
	tensile strength	Break,23°C	ASTM D638	28.0	MPa
	tensile strength	tensile strength	Break,23°C,4.00mm	ISO 527-2	28.0	MPa
elongation	Yield,23°C	ASTM D638	4.3	%
elongation	elongation	Yield,23°C,4.00mm	ISO 527-2	4.2	%
tensile strength	Yield,23°C	ASTM D638	50.0	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	70.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	64.0	°C
Vicat softening temperature	--	ASTMD15254	85.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B	76.0	°C
specific heat	60°C		1300	J/kg/°C
	specific heat	240°C		2000	J/kg/°C
	specific heat	specific heat	导热系数(23°C)		0.19	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	--	ASTM D792	1.27	g/cm³
density	density	23°C	ISO 1183	1.27	g/cm³
Shrinkage rate	MD：3.20mm	ASTM D955	0.20to0.50	%
Water absorption rate	23°C,24hr	ASTMD570	0.13	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	1E+16	ohms
Volume resistivity	23°C	ASTM D257	1E+15	ohms·cm
Dielectric strength	23°C	ASTM D149	16	kV/mm
Arc resistance		ASTM D495	158	sec
Dielectric constant	23°C,1kHz	ASTM D150	2.60
Dielectric constant	Dielectric constant	23°C,1MHz	ASTM D150	2.40
Dissipation factor	23°C,1kHz	ASTM D150	5E-03
Dissipation factor	Dissipation factor	23°C,1MHz	ASTM D150	0.017
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale,23°C	ASTM D785	106

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.