POM K900 KOLON KOREA

Form：Granules | Grade：Injection grade

Properties:

High impact resistanceHigh mobility

Typical Applications:

High impact resistanceHigh mobilityThin walled components

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	High impact resistance \| High mobility \| Thin walled components
Properties:	High impact resistance \| High mobility

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ASTM D256	50	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield,23°C	ASTM D638	64.0	Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	65.0	Mpa
bending strength	23°C	ISO 178	92.0	Mpa
bending strength	bending strength	23°C	ASTM D790	96.0	Mpa
Bending modulus	23°C	ISO 178	2950	Mpa
elongation	Yield,23°C	ASTM D638	45	%
Tensile strain	Break,23°C	ISO 527-2	20	%
Bending modulus	23°C	ASTM D790	2700	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ASTM D696	1.3E-04	cm/cm/°C
Melting temperature			166	°C
Melting temperature	Melting temperature		ISO 11357-3	165	°C
Vicat softening temperature		ASTM D1525	162	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	100	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	110	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	158	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,60%RH	ASTM D570	0.22	%
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.22	%
Shrinkage rate	MD	ISO 294-4	1.9	%
	Shrinkage rate	TD	ISO 294-4	1.9	%
	Shrinkage rate	Shrinkage rate	MD	ASTM D955	2.0	%
density		ASTM D792	1.41	g/cm³
density	density		ISO 1183	1.41	g/cm³
melt mass-flow rate	190°C/2.16kg	ASTM D1238	42	g/10min
melt mass-flow rate	melt mass-flow rate	190°C/2.16kg	ISO 1133	42	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		IEC 60243-1	19	KV/mm
Dielectric strength	Dielectric strength		ASTM D149	19	KV/mm
Volume resistivity		IEC 60093	1E+14	ohms·cm
Volume resistivity	Volume resistivity		ASTM D257	1E+14	ohms·cm
Surface resistivity		IEC 60093	1E+16	ohms
Surface resistivity	Surface resistivity		ASTM D257	1E+16	ohms
Dielectric constant		ASTM D150	3.70
Dissipation factor	1MHz	ASTM D150	6E-03
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	94
Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	80

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.