Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.80到2.00 g/cm³ |
| Apparent density | | ISO60 | 0.75到0.90 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.15到0.45 % |
| Water absorption rate | | ISO62 | <0.20 % |
| PostShrinkage | | ISO2577 | <0.050 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 875 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compression stress | | ISO604 | 150到200 MPa |
| Tensile modulus | Injection | ISO527-2 | 10000到14000 MPa |
| Tensile stress | Injection | ISO527-2 | 80.0到90.0 MPa |
| Flexural modulus | Injection | ISO178 | 11000到14000 MPa |
| Bending stress | Injection | ISO178 | 120到160 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 3.5到4.5 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 7.0到10 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | >500 V |
| Surface Resistivity | | IEC60093 | 1.0E+14到1.0E+15 ohms |
| Volume resistivity | | IEC60093 | 1.0E+14到1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 15到20 kV/mm |
| | IEC60250 | 4.505.00 |
| | IEC60250 | 4.004.50 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | >200 °C |
| | ISO75-2/C | 130到150 °C |
| | ISO11359-2 | 5.0E-6到1.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.90到1.1 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.