Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Apparent density | | | 0.59to0.64 g/cm³ |
melt mass-flow rate | | ASTM D1238 | 6.0 g/10min |
Shrinkage rate | | ASTM D955 | 0.40-0.70 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | | ASTM D785 | 75 |
optical performance | Test Condition | Test Method | Test Result |
---|
refractive index | | ASTM D542 | 1.590 |
transmissivity | | ASTM D1003 | 88.0to90.0 % |
OpticalDensity-400-700nmavg | | | 0.0460 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ASTM D638 | 2960 Mpa |
tensile strength | | ASTM D638 | 46.9 Mpa |
elongation | | ASTM D638 | 2.0 % |
Flexural modulus | | ASTM D790 | 3310 Mpa |
bending strength | | ASTM D790 | 96.5 Mpa |
Electrical performance | Test Condition | Test Method | Test Result |
---|
dielectric strength | | ASTM D149 | 20 KV/mm |
dielectric constant | | ASTM D150 | 2.50 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | | 93.3 °C |
vicat | | ASTM D15254 | 106 °C |
Linear coefficient of thermal expansion | | ASTM D696 | 7.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.