Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 2.09 g/cm³ |
| Shrinkage rate | | ASTM D995 | 0.13 % |
| Shrinkage rate | | ASTM D995 | 0.25 % |
| Water absorption rate | | ASTM D570 | 0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 121 R |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 128 MPa |
| elongation at break | | ASTM D638 | 0.70 % |
| bending strength | | ASTM D790 | 193 MPa |
| Flexural modulus | | ASTM D790 | 20600 MPa |
| Impact strength of cantilever beam gap | | ASTM D256 | 100 J/m |
| Impact strength of cantilever beam gap | | ASMTD638 | 26500 MPa |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL -94 | V-0 3.00mm |
| UL flame retardant rating | | UL -94 | V-0 0.75mm |
| UL flame retardant rating | | UL -94 | V-0 1.50mm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D150 | 0.053 |
| Dissipation Factor | | ASTM D150 | 0.0083 |
| Dissipation Factor | | ASTM D495 | 182 s |
| Dissipation Factor | | ASTM D257 | 1E+15 Ω.cm |
| dielectric strength | | ASTM D149 | 11.0 KV/mm |
| dielectric constant | | ASTM D150 | 5.5 1kHz |
| dielectric constant | | ASTM D150 | 5.3 1MHz |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | >=260 °C |
| Heat distortion temperature | | | 282 °C |
| Heat distortion temperature | | | 1.4E-05 cm/cm／°C |
| Heat distortion temperature | | | 3.2E-05 cm/cm／°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.