Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ASTM D1895 | 0.61 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.41 % |
| Water absorption rate | | ASTM D570 | 0.48 % |
| density | | ASTM D792 | 1.39 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 84 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM D2863 | 29 % |
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ASTM D256 | 18.7 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 15 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 7960 MPa |
| tensile strength | | ASTM D638 | 62.0 MPa |
| Flexural modulus | | ASTM D790 | 7370 MPa |
| bending strength | | ASTM D790 | 90.8 MPa |
| compressive strength | | ASTM D695 | 215 MPa |
| elongation | Break | ASTM D638 | 0.90 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 13 kV/mm |
| dielectric strength | | ASTM D149 | 9.5 kV/mm |
| dielectric constant | | ASTM D150 | 5.40 |
| Dissipation Factor | | ASTM D150 | 0.041 |
| arc resistance | | ASTM D495 | 87.0 sec |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 3 |
| Volume resistivity | | ASTM D257 | 3E+13 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 185 °C |
| Continuous use temperature | | ASTM D794 | 203 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 6.3E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.37 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.