PLA F 1138
0
- Usages:Filmbag
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO1133 | 2.0到4.5 g/10min | |
| Melt volume flow rate | ISO1133 | 1.50到3.50 cm³/10min | |
| density | ISO1183 | 1.47 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | Yield | ISO527-2 | 16.0 MPa |
| Break | ISO527-2 | 14.0 MPa | |
| Tensile strain | Break | ISO527-2 | 370 % |
| Flexural modulus | ISO178 | 390 MPa | |
| Bending stress | ISO178 | 10.0 MPa | |
| TensileStrength | ISO527 | 360 % | |
| Tensile modulus | ISO527-2 | 405 MPa | |
| Fracture bending strain | ISO178 | NoBreak |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ISO527-3 | 280 % | |
| ISO527-3 | 400 % | ||
| Tear resistant ductility | ISO6383-2 | 140 kN/m | |
| ISO6383-2 | 300 kN/m | ||
| Film thickness - tested | 20 µm | ||
| Tensile modulus | ISO527-3 | 530 MPa | |
| ISO527-3 | 465 MPa | ||
| Tensile stress | ISO527-3 | 30.0 MPa | |
| ISO527-3 | 22.0 MPa | ||
| ISO527-3 | 29.0 MPa | ||
| ISO527-3 | 21.0 MPa | ||
| elongation | ISO527-3 | 280 % | |
| ISO527-3 | 400 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO3146 | >155 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.