PP 5C20800

Compare

Technical Data Sheet

physical property	Test Method	Test Result
density	ISO 1183	0.905 g/cm³
Apparent density	ISO 60	0.50-0.60 g/cm³
	ISO 1133	15-25 g/10 min
density	ISO1183	0.905 g/cm³
Apparent density	ISO60	0.50到0.60 g/cm³
melt mass-flow rate	ISO1133	15到25 g/10min
Density Anneled	ISO1872	905 kg/m³

flammability	Test Method	Test Result
UL flame retardant rating	UL94	HB
Hot filament ignition temperature	IEC60695-2-13	650 °C
UL flame retardant rating	UL 94	HB
Hot filament ignition temperature	IEC 60695-2-13	650 °C

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/5	1300 MPa
Tensile stress		ISO 527-2/5	28.0 MPa
Tensile stress	Tensile stress		ISO 527-2/5	24.0 MPa
Tensile strain		ISO 527-2/5	50 %
Flexural modulus		ISO 178	1050 MPa
Impact strength of cantilever beam gap		ISO 180/1A	7 kJ/m²
Tensile modulus		ISO527-2/5	1300 MPa
Tensile stress		ISO527-2/5	24.0 MPa
Tensile stress	Tensile stress		ISO527-2/5	28.0 MPa
Tensile strain		ISO527-2/5	50 %
Flexural modulus		ISO178	1050 MPa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ISO180/1A	7.0 kJ/m²

Thermal performance	Test Method	Test Result
vicat	ISO306/B	67.0 °C
melting temperature	ISO11357	165 °C
vicat	ISO 306/B	67.0 °C
melting temperature	ISO 11357	165 °C
	ISO 75-2/B	88 °C
		ISO75-2/B	88.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.