TPU 2785 NINGBO KINGSUI

Form：Granules | Grade：Pipe grade

Properties:

Low temperature resistanc

Typical Applications:

filmWire and cable

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	film \| Wire and cable
Properties:	Low temperature resistanc

Certificates

No Data...

Technical Data Sheet

machinability	Test Condition	Test Method	Test Result	Test Unit
Dry conditions			85℃ 3小时
Processing temperature			140－160	°C
	Processing temperature			175－185	°C
		Processing temperature			170－180	°C
		Processing temperature	Processing temperature			180－190	°C
Mold temperature			20－30	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	100%	ASTM D412/ISO 527	6.0	Mpa/Psi
Tensile modulus	Tensile modulus	300%	ASTM D412/ISO 527	11	Mpa/Psi
tensile strength		ASTM D412/ISO 527	40	Mpa/Psi
tear strength		ASTM D624/ISO 34	110	n/mm²
Shore hardness		ASTM D2240/ISO 868	85+_2	Shore A
Resilience		ASTM D2630/ISO 4662	45	%
Tensile stress	100%伸长率	ISO 37:2005(E)	6.0	Mpa
Tensile stress	Tensile stress	300%伸长率	ISO 37	11	Mpa
tensile strength		ISO 37	40	Mpa
elongation	Break	ISO 37	520	%
tear strength		ISP 34-1:2004(E)	110	kN/m
Resilience		ISO 4662	45	%
Friction coefficient		DIN 53516	27	mg
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Glass transition temperature		ASTM D3418/ISO 815	-40	℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	100	℃（℉）
Vicat softening temperature	Vicat softening temperature		ISO 306	100	°C
Glass transition temperature (Tg)		ASTM D3417	-40	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 2781/JIS K7311	1.19
Shore hardness		ISO 868:2006(E)	85±2/-

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.