Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:100 |
| Hardener | | 按重量计算的混合比:19 |
| | | 6.0 min |
| | | 15 min |
| | | 16 hr |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Curing Time | | | 1.0 hr |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.14 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore A | ASTMD2240 | 95 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| AbrasionIndex-NBS | | | 300 |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ASTMD412 | 12.4 MPa |
| Tensile stress | | ASTMD412 | 23.4 MPa |
| tensile strength | | ASTMD412 | 34.5 MPa |
| elongation | Break | ASTMD412 | 400 % |
| tear strength | | ASTMD624 | 87.6 kN/m |
| tear strength | Split | ASTMD470 | 26 kN/m |
| compression set | | ASTMD395B | 40 % |
| Basho elasticity | | ASTMD2632 | 40 % |
| Kappa modulus | | ASTMD1043 | 552 MPa |
| Kappa modulus | | ASTMD1043 | 114 MPa |
| Kappa modulus | | ASTMD1043 | 49.3 MPa |
| Kappa modulus | | ASTMD1043 | 16.5 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | ASTMC177 | 0.12 W/m/K |
| brittle temperature | | ASTMD746 | <-70.0 °C |
| | ASTMD696 | 2.3E-04 cm/cm/°C |
| | ASTMD696 | 1.6E-04 cm/cm/°C |
| | ASTMD696 | 1.6E-04 cm/cm/°C |
| | ASTMD696 | 1.2E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.