GPPS 147F BASF KOREA

Form：Granules | Grade：Injection grade

Properties:

Easy to processGood heat resistanceModerate liquidityUniversal type with good

Typical Applications:

Transparent parts of refrigeratorHousehold daily necessitieschipMonitor

Supplier(1)

Product Description

Certificates(1)

Datasheet

Alternative Model(1)

Product Description

Typical Applications:	Transparent parts of refrigerator \| Household daily necessities \| chip \| Monitor
Properties:	Easy to process \| Good heat resistance \| Moderate liquidity \| Universal type with good

Certificates

TDS

Technical Data Sheet

machinability	Test Condition	Test Method	Test Result	Test Unit
Linear mold shrinkage rate		ISO 294-4	0.3 - 0.6	%
Melting temperature range		ISO 294	180 - 260	℃
Mold temperature range		ISO 294	10 - 60	℃
Injection speed		ISO 294	200	mm/s
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	200℃ / 5kg	ISO 1133	6.5	cm3/10min
Charpy Notched Impact Strength	23℃	ISO 179	3	kJ/m²
Impact strength of simply supported beam without notch	23℃	ISO 179	17	kJ/m²
Tensile yield strength	23℃	ISO 527	50	Mpa
Tensile strain at break	23℃	ISO 527	3	%
Tensile modulus		ISO 527	3300	Mpa
bending strength		ISO 178	98	Mpa
Ball Pressure Test		ISO 2039-1	150	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	50N, 50℃/h	ISO 306	95	℃
Vicat softening temperature	Vicat softening temperature	10N, 50℃/h	ISO 306	100	℃
Hot deformation temperature	1.8MPa, Annealed4h/80℃	ISO 75	85	℃
Hot deformation temperature	Hot deformation temperature	0.45MPa, Annealed4h/80℃	ISO 75	93	℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1046	kg/m3
Water absorption rate	23℃ Saturation	ISO 62	<0.1	%
Water absorption rate	Water absorption rate	23℃, 50%RH Equilibrium	ISO 62	<0.1	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
breakdown voltage	短时，1.5 mm	IEC 60243-1	135	KV/mm
Dielectric constant	100Hz	IEC 60250	2.5	-
Dielectric constant	Dielectric constant	1MHz	IEC 60250	2.5	-
Volume resistivity		IEC 60093	>1E16	ohm·m
Surface resistivity		IEC 60093	>1E14	Ohm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.