| physical property | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | ISO 11443-A | 250 Pa·s |
| density | | ISO 1183 | 1.38 g/cm³ |
| Shrinkage rate | | ISO 2577 | 0.30to0.50 % |
| Shrinkage rate | | ISO 2577 | 0.15to0.35 % |
| Water absorption rate | | ISO 62 | 0.40 % |
| Water absorption rate | | ISO 62 | 0.10 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/A | 11 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 12 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 40 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 10000 MPa |
| tensile strength | | ISO 527-2/5 | 135 MPa |
| Tensile strain | | ISO 527-2/5 | 2.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 35 kV/mm |
| relative permittivity | | IEC 60250 | 3.60 |
| relative permittivity | | IEC 60250 | 3.40 |
| Dissipation Factor | | IEC 60250 | 3E-03 |
| Dissipation Factor | | IEC 60250 | 8.5E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Surface Resistivity | | IEC 60093 | 1E+17 ohms |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 134 °C |
| Heat distortion temperature | | ISO 75-2/A | 126 °C |
| vicat | | ISO 306/B50 | 132 °C |
| vicat | | ISO 306/B120 | 134 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.