PC SI-3109G K2007 BK Samsung Cheil South Korea

Form：Granules | Grade：Injection grade

Properties:

Carbon fiber flame retardUV resistance High glossFiller: Glass fiber reinf

Typical Applications:

Electronic and electrical componentsAutomotive componentsElectronic and electric products

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic and electrical components \| Automotive components \| Electronic and electric products
Properties:	Carbon fiber flame retard \| UV resistance \| High gloss \| Filler: Glass fiber reinf

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.9	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	V-2
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200℃ 5kg	ASTM D-1238	21.0	g/10min
Water absorption rate	24hrimmersion	ASTM D-570	0.15	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	88.0	Mpa
bending strength	bending strength		ASTM D790	88.3	Mpa
Bending modulus		ISO 178	2600	Mpa
Bending modulus	Bending modulus		ASTM D790	2450	Mpa
Tensile strain	Break	ISO 527-2/50	15	%
elongation	Break	ASTM D638	47	%
tensile strength	Break	ISO 527-2/50	46.0	Mpa
	tensile strength	Break	ASTM D638	47.1	Mpa
		tensile strength	Yield	ISO 527-2/50	57.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	55.9	Mpa
Tensile modulus		ISO 527-2/50	2400	Mpa
Tensile modulus	Tensile modulus		ASTM D638	2160	Mpa
tensile strength	5mm/min	ASTM D-638	570	Kgf/cm
Impact strength of cantilever beam gap	1/8"	ASTM D-256	9	Kgf.cm/cm
Rockwell hardness		ASTM D-785	89	R-Scale
bending strength	2.8mm/min	ASTM D-790	1100	Kgf/cm
Bending modulus	2.8mm/min	ASTM D-790	29000	Kgf/cm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B120	147148	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	145146	°C
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	128	°C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	127	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	131	°C
			Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	140	°C
				Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	142	°C
					Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	140	°C
					Hot deformation temperature	Hot deformation temperature	1/4" 18.56kgf/cm	ASTM D-648	120	°C
Vicat softening temperature	5kg	ASTM D-1525	N/A	°C
UL flame retardant rating		UL 94	0.8 V-2
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD：3.20mm	ASTM D955	0.30-0.50	%
melt mass-flow rate	250°C/2.16kg	ISO 1133	19	g/10min
melt mass-flow rate	melt mass-flow rate	250°C/10.0kg	ASTM D1238	20	g/10min
ash content		ISO 3451	9.8	%
Shrinkage rate		ASTM D-955	0.3-0.5	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	89
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC SI-3109G K2007 BK Samsung Cheil South Korea

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index