ULDPE 4203 STYRON US

Form：Granules | Grade：Blow molding grade

Properties:

High impact resistanceLow temperature resistancCompliant with Canadian HExcellent elasticity andResistance to cracking an

Typical Applications:

filmcontainerchipUsed for packaging

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	film \| container \| chip \| Used for packaging
Properties:	High impact resistance \| Low temperature resistanc \| Compliant with Canadian H \| Excellent elasticity and \| Resistance to cracking an

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transparency	20μm	ASTM D1746	93
gloss	20 μm	ASTM D2457	48
turbidity		ASTM D1003	5	%
gloss	45°	ASTM D2457	39
turbidity		ASTM D1003	14	%
Other performance	Test Condition	Test Method	Test Result	Test Unit
Starting temperature of heat sealing		陶氏企业测试	88	°C
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238	0.8	g/10min
density		ASTM D792	0.905
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Puncture intensity	(20 μm)	陶氏企业测试	22	J/cm
tensile strength	Yield	ASTM D882	9	Mpa
tensile strength	tensile strength	20 μm (MD)	ASTM D882	53	Mpa
Elongation at Break	20μm (MD)	ASTM D882	445	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D1525	84	°C
Vicat softening temperature	Vicat softening temperature		ASTM D1525	83.9	°C
Melting temperature		Internal Method	123	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190°C/2.16kg	ASTM D1238	0.80	g/10min
film	Test Condition	Test Method	Test Result	Test Unit
film thickness			25	µm
Thin film puncture strength		Internal Method	4.52	J
	Thin film puncture strength		Internal Method	48.9	N
	Thin film puncture strength	Thin film puncture strength		Internal Method	24.8	J/cm³
Membrane strength	MD	ASTM D882	45.5	J/cm³
Membrane strength	Membrane strength	TD	ASTM D882	64.5	J/cm³
Secant modulus	1%Secant,MD	ASTM D882	98.6	Mpa
	Secant modulus	2%Secant,MD	ASTM D882	89.6	Mpa
		Secant modulus	1%Secant,TD	ASTM D882	113	Mpa
		Secant modulus	Secant modulus	2%Secant,TD	ASTM D882	93.8	Mpa
tensile strength	MD:Yield	ASTM D882	6.21	Mpa
	tensile strength	TD:Yield	ASTM D882	5.86	Mpa
		tensile strength	MD:Break	ASTM D882	32.4	Mpa
		tensile strength	tensile strength	TD:Break	ASTM D882	30.0	Mpa
elongation	MD:Break	ASTM D882	340	%
elongation	elongation	TD:Break	ASTM D882	570	%
Dart impact		ASTM D1709B	>1100	g
Elmendorf tear strength	MD	ASTM D1922	370	g
Elmendorf tear strength	Elmendorf tear strength	TD	ASTM D1922	520	g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.