PC SC-1100R00 Samsung Cheil South Korea

Form：Granules | Grade：Blow molding grade

Properties:

Medium viscosityElectrical performanceFlame retardantHigh impact resistance

Typical Applications:

Industrial componentsAutomotive ApplicationsElectrical applicationsAutomotive External Parts

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Industrial components \| Automotive Applications \| Electrical applications \| Automotive External Parts
Properties:	Medium viscosity \| Electrical performance \| Flame retardant \| High impact resistance

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.830mm	UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--3	ASTM D638	2260	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/50	2300	Mpa
tensile strength	Yield3	ASTM D638	62.8	Mpa
	tensile strength	Yield	ISO 527-2/50	64.0	Mpa
		tensile strength	Break3	ASTM D638	62.8	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	64.0	Mpa
elongation	Break3	ASTM D638	110	%
elongation	elongation	Break	ISO 527-2/50	110	%
Bending modulus	--4	ASTM D790	2260	Mpa
Bending modulus	Bending modulus	--5	ISO 178	2300	Mpa
bending strength	--4	ASTM D790	90.2	Mpa
bending strength	bending strength	--5	ISO 178	92.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Hot air dryer			80	°C
Vacuum drying machine			80	°C
Hot air dryer			3.0 to 4.0	hr
Vacuum drying machine			4.0 to 6.0	hr
Suggested maximum moisture content			0.040	%
Temperature at the rear of the barrel			100 to 260	°C
Temperature in the middle of the barrel			260 to 270	°C
Temperature at the front of the material cylinder			260 to 280	°C
Spray nozzle temperature			280	°C
Mold temperature			80 to 110	°C
Injection pressure			98.1	Mpa
Back pressure			0.981 to 1.96	Mpa
Screw speed			30 to 50	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	137	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	127	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	125	°C
Vicat softening temperature		ISO 306/B50	146	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	12	g/10 min
Shrinkage rate	Flow : 3.20 mm	ASTM D955	0.50 - 0.70	%
	Shrinkage rate	Across FlowFlow : 3.20 mm	ASTM D955	0.50 - 0.70	%
		Shrinkage rate	横向Flow : 2.00 mm	ISO 294-4	0.50 - 0.70	%
		Shrinkage rate	Shrinkage rate	Flow : 2.00 mm	ISO 294-4	0.50 - 0.70	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	120
Rockwell hardness	Rockwell hardness	R -Sale	ISO 2039-2	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.