| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| density | | ISO 1183 | 1.19 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.20-0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 105 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 91.0 % |
| transmissivity | | ASTM D1003 | 89.0 % |
| Haze ratio | | ASTM D1003 | 0.30 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 1900 Mpa |
| Flexural modulus | | ISO 178 | 1750 Mpa |
| bending strength | | ISO 178 | 64.0 Mpa |
| bending strength | | ASTM D790 | 67.0 Mpa |
| tensile strength | | ASTM D638 | 46.0 Mpa |
| tensile strength | | ISO 527-2 | 47.0 Mpa |
| tensile strength | | ASTM D638 | 53.0 Mpa |
| tensile strength | | ISO 527-2 | 49.0 Mpa |
| elongation | | ASTM D638 | 5.0 % |
| Tensile strain | | ISO 527-2 | 4.0 % |
| elongation | | ASTM D638 | 310 % |
| Tensile strain | | ISO 527-2 | 210 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 60 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 370 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 6.3 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 30 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D4812 | NoBreak |
| Impact strength of cantilever beam gap | | ASTM D4812 | NoBreak |
| Dart impact | | ASTM D3763 | 48.0 J |
| Dart impact | | ASTM D3763 | 45.0 J |
| Multi axis Instrumented Impact Energy | | ISO 6603-2 | 55.0 J |
| Multi axis Instrumented Impact Energy | | ISO 6603-2 | 71.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTM D495 | 123 sec |
| Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 0 |
| Volume resistivity | | ASTM D257 | 1E+17 ohms·cm |
| dielectric strength | | ASTM D149 | 17 KV/mm |
| dielectric constant | | ASTM D150 | 2.60 |
| dielectric constant | | ASTM D150 | 2.60 |
| dielectric constant | | ASTM D150 | 2.50 |
| dielectric constant | | ASTM D150 | 2.50 |
| Dissipation Factor | | ASTM D150 | 6E-03 |
| Dissipation Factor | | ASTM D150 | 0.012 |
| Dissipation Factor | | ASTM D150 | 0.015 |
| Dissipation Factor | | ASTM D150 | 0.015 |
| Surface Resistivity | | ASTM D257 | 1E+17 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 73.0 °C |
| Heat distortion temperature | | ISO 75-2/B | 73.0 °C |
| Heat distortion temperature | | ASTM D648 | 65.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 66.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.