Technical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 注射成型 |
| purpose | | | 喷淋. 周转箱. 油漆筒 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-1505 | 0.926 g/cm |
| melt mass-flow rate | | ASTM D-1238 | 8.5 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 8.0 kg·cm/cm(J/M)ft·lb/in |
| Flexural modulus | | ASTM D790/ISO 178 | 12000 kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D-638 | 260 kg/cm |
| tensile strength | | ASTM D-638 | 100 kg/cm |
| Impact strength of cantilever beam gap | | ASTM D-256 | 8.0 kg.cm/cm |
| elongation | | ASTM D-638 | >500 % |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D-790 | 12000 kg/cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.962 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 8.5 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D1525/ISO R306 | 124 ℃（℉） |
| vicat | | ASTM D-1525 | 124 °C |
| brittle temperature | | ASTM D-746 | ＜-80 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.