Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.03 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 9.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 91 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Smoke density | | ASTME662 | 120 |
| Smoke density | | ASTME662 | 49 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 825 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 29 % |
| VW | | UL 1581 | Pass |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ISO 527-2/50 | 160 % |
| Flexural modulus | | ASTM D790 | 100 MPa |
| Flexural modulus | | ISO 178 | 78.0 MPa |
| tensile strength | Break | UL 1581 | 24.0 MPa |
| tensile strength | | ASTM D638 | 15.0 MPa |
| tensile strength | | UL 1581 | 23.5 MPa |
| tensile strength | Break | ISO 527-2/50 | 14.0 MPa |
| elongation | Break | UL 1581 | 270 % |
| elongation | | ASTM D638 | 170 % |
| elongation | | UL 1581 | 230 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 3.3E+16 ohms·cm |
| dielectric strength | | IEC 60243-1 | 22 kV/mm |
| dielectric constant | | ASTM D150 | 2.60 |
| Dissipation Factor | | ASTM D150 | 0.033 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | <-40.0 °C |
| Heat distortion temperature | | UL 1581 | 5.0 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.