PET

PET EPIMIX PBT/PET GFR 30 NC EPSAN TURKEY

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23℃	N.m	469.91to626.55
Impact strength of simply supported beam without notch	23℃	kJ/m²	5.572to15.323
Charpy Notched Impact Strength	23℃	kJ/m²	1.067to2.229

flammability	Test Method	Test Result
Burning wire flammability index	°C	648to960
Extreme Oxygen Index	%	21
Burning rate	mm/min	0.0to99.06
Hot filament ignition temperature	°C	643to960

mechanical properties	Test Condition	Test Method	Test Result
yield			163.45to172.41 Mpa
yield	yield			87.59to175.17 Mpa
crack		%	1.7-3.9
yield		%	1.0-4.5
crack			97.24to160.0 Mpa
yield		%	1.0-3.0
crack			50.0to140.69 Mpa
yield			89.66to140.69 Mpa
crack		%	1.5-3.2

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		°C	237to240
transverse		mm/mm/°C	83.8E-5-152.4E-5
RTI		°C	75to140
RTI Elec		°C	75to140
RTI Imp		°C	75to125
transverse		mm/mm/°C	76.2E-5-101.6E-5
flow		mm/mm/°C	27.9E-5-50.8E-5
flow	flow		mm/mm/°C	30.5E-5-50.8E-5
thermal conductivity	23℃	W/m2k	0.30to0.33

Physical properties	Test Condition	Test Method	Test Result
saturated		%	0.30-0.40
Apparent density		g/cm³	0.70-0.80
melt mass-flow rate	265°C/2.16kg	g/10min	17to22
Viscosity value	23℃	ml/g	80.0-95.0
Melt Volume Flow Rate (MVR)	260°C/2.16kg	cm³/10min	0.05to0.07
balance		%	0.055-0.21
Lateral flow		mm/mm	188.0E-3-208.3E-3
flow		mm/mm	86.4E-3-0.330

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	23℃		8.0E-4-0.017
Surface resistivity		ohms	1.0E+14-1.1E+15
Volume resistivity	23℃	ohms·cm	1.0E+12-1.0E+16
Relative permittivity	23℃		3.76
Compared to the anti leakage trace index		V	PLC 2

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	23℃		110to120
Ball Pressure Test			110.34to251.72 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.