Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 0.6(0.9) % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D-570 | 0.4(3.8) % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D-790 | 6000(4000) Mpa |
| elongation | | ASTM D-638 | 3(3) % |
| tensile strength | | ASTM D-638 | 110(90) Mpa |
| Impact strength of cantilever beam gap | | ASTM D-256 | 50(55) J/m |
| bending strength | | ASTM D-790 | 180(150) Mpa |
| Rockwell hardness | | ASTM D-785 | 105 M Scale |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Glass Fiber Content | | | 15 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D-150 | 0.020 |
| Volume resistivity | | ASTM D-257 | 10 Ω.cm |
| dielectric constant | | ASTM D-150 | 4.2 |
| dielectric strength | | ASTM D-149 | 25 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D-648 | 295 °C |
| Linear coefficient of thermal expansion | | ASTM D-696 | 3.4(3.5) |
| UL flame retardant rating | | UL 94 | HB |
| melting temperature | | | 310 °C |
| Glass transition temperature (Tg) | | | 85 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.