Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 20 g/10min |
| Shrinkage rate | | ASTM D955 | 0.40to0.70 % |
| Water absorption rate | | ASTM D570 | 0.030 % |
| density | | ASTM D792 | 1.04 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 100 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 15 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 2940 MPa |
| bending strength | | ASTM D790 | 71.6 MPa |
| tensile strength | | ASTM D638 | 40.2 MPa |
| elongation | Break | ASTM D638 | 4.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | | UL 746 | PLC 3 |
| Volume resistivity | | ASTM D257 | 1E+17 ohms·cm |
| dielectric constant | | ASTM D150 | 2.60 |
| arc resistance | | ASTM D495 | PLC7 |
| arc resistance | | ASTM D495 | PLC7 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
| High arc combustion index (HAI) | | UL 746 | PLC 4 |
| High arc combustion index (HAI) | | UL 746 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 75.0 °C |
| vicat | | ASTM D15251 | 87.0 °C |
| vicat | | ASTM D15252 | 82.0 °C |
| RTI Elec | | UL 746 | 50.0 °C |
| RTI Elec | | UL 746 | 50.0 °C |
| RTI Imp | | UL 746 | 50.0 °C |
| RTI Imp | | UL 746 | 50.0 °C |
| RTI | | UL 746 | 50.0 °C |
| RTI | | UL 746 | 50.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.