ABS 5000S TAIDA TAIWAN

Form：Granules | Grade：Injection grade

Properties:

High rigidityantioxidantGood tensile strengthHigh steel typeInjection moldingHigh rigidity and impact

Typical Applications:

Charger casingIndustrial applicationsropeBagMonofilamentFor audio tapesclockHousehold productsRecording tape case etcElectrical appliancesHousehold goodsAudiotape

Supplier(0)

Product Description

Certificates(4)

Datasheet

Product Description

Typical Applications:	Charger casing \| Industrial applications \| rope \| Bag \| Monofilament \| For audio tapes \| clock \| Household products \| Recording tape case \| etc \| Electrical appliances \| Household goods \| Audiotape
Properties:	High rigidity \| antioxidant \| Good tensile strength \| High steel type \| Injection molding \| High rigidity and impact

Certificates

TDS

TDS_ISO

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	160	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	150	J/m
machinability	Test Condition	Test Method	Test Result	Test Unit
Relative Heat Index (RTI)		UL -746B	60	°C
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D-792	1.04
Water absorption rate		ASTM D-570	0.3	wt%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	1/8"，Break	ASTM D-638	5400	psi
Elongation at Break	1/8"	ASTM D-638	20	%
bending strength	23℃ 2.8mm/min	ASTM D-790	800	kg/cm
bending strength	bending strength	23℃ 2.8mm/min	ASTM D-790	11400	psi
flexural coefficient	23℃ 2.8mm/min	ASTM D-790	30000	kg/cm
flexural coefficient	flexural coefficient	23℃ 2.8mm/min	ASTM D-790	420000	psi
Rockwell hardness			119
Impact strength of cantilever beam gap	23℃1/2"	ASTM D-256	13 (2.4)	kg.cm/cm(ft.1b/in)
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃1/8"	ASTM D-256	16 (2.9)	kg.cm/cm(ft.1b/in)
tensile strength	23℃，Yield	ASTM D-638	480	kg/cm
	tensile strength	23℃，Yield	ASTM D-638	6800	psi
		tensile strength	1/8"，Break	ASTM D-638	380	kg/cm
		tensile strength	tensile strength	Break,23°C,3.18mm	ASTM D638	37.2	Mpa
elongation	Break,23°C,3.18mm	ASTM D638	20	%
Bending modulus	23°C	ASTM D790	2900	Mpa
bending strength	Yield,23°C	ASTM D790	78.6	Mpa
tensile strength	Yield,23°C,3.18mm	ASTM D638	46.9	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	Unannealed	ASTM D-648	89 (192)	℃(F)
Vicat softening temperature		ASTM D-1525	104	°C
UL flame retardant rating		UL 94	HB
Resistance to hot wire combustion		UL -746A	15	Sece
RTI Imp	1.6mm	UL 746	60.0	°C
RTI Str	1.6mm	UL 746	60.0	°C
Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	83.0	°C
Vicat softening temperature		ASTM D15254	104	°C
RTI Elec	1.6mm	UL 746	60.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ASTM D-955	0.4	%
density		ASTM D792	1.04	g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	2.3	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	23	g/10min
Shrinkage rate	MD	ASTM D955	<0.40	%
Water absorption rate	24hr	ASTM D570	<0.30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Arc resistance		UL -746A	15	Arcs
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ASTM D785	119

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.