Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | 内部方法 | 1.15到1.25 g/cm³ |
| Shrinkage rate | | 内部方法 | 1.7 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore A | 内部方法 | 39到49 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | 51 mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| OzoneResistance | | ASTMD518/1149 | NoCracking |
| Temperature LongTermUpperService | | | >125 °C |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ASTMD412 | 2.07 MPa |
| tensile strength | Yield | ASTMD412 | 4.14 MPa |
| elongation | Break | ASTMD412 | 700 % |
| tear strength | | ASTMD624 | 17.5 kN/m |
| compression set | | ASTMD395B | 15 % |
| compression set | | ASTMD395 | 38 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| Change rate of ultimate elongation in air | | ASTMD573 | 25 % |
| The rate of change in hardness of an air hardness tester | | ASTMD573 | 2.0 |
| Change rate of tensile strength in air | | ASTMD573 | 35 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTMD746 | -52.8 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.