Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 0.926 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 1.0 g/10min |
| processability | Test Condition | Test Method | Test Result |
|---|
| Melt Temperature | | | 207-216 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D-2457 | 80 |
| Haze ratio | | ASTM D-1003 | 9 % |
| gloss | | ASTMD2457 | 80 |
| Haze ratio | | ASTMD1003 | 9.0 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 0.926 g/m3 |
| melt mass-flow rate | | ASTM D-1238 | 1 g/10min |
| film thickness | | | 38.1 um |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile elongation at break (MD) | | ASTM D-882 | 630 % |
| Tensile elongation at break (TD) | | ASTM D-882 | 740 % |
| Falling hammer impact | | ASTM D-1709A | 220 g |
| Elmendorf Tear Strength (TD) | | ASTM D-1922 | 590 g |
| Elmendorf Tear Strength (MD) | | ASTM D-1922 | 250 |
| Tangent modulus (MD) | | ASTM D-882 | 235 Mpa |
| Tangent modulus (TD) | | ASTM D-882 | 281 Mpa |
| Tensile yield strength (MD) | | ASTM D-882 | 13.2 Mpa |
| Tensile yield strength (TD) | | ASTM D-882 | 14.7 Mpa |
| Tensile strength at break (MD) | | ASTM D-882 | 47.8 Mpa |
| Tensile fracture strength (TD) | | ASTM D-882 | 42.3 Mpa |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Film Piercing Resistance Movement | | Internal Method | 3.06 J/cm³ |
| Film Resilience (TD) | | ASTM D-882 | 140 J/cm³ |
| Film Resilience (MD) | | ASTM D-882 | 128 J/cm4 |
| film | Test Condition | Test Method | Test Result |
|---|
| Film thickness - tested | | | 38 µm |
| Membrane puncture resistance | | 内部方法 | 3.06 J/cm³ |
| film strength | | ASTMD882 | 128 J/cm³ |
| film strength | | ASTMD882 | 140 J/cm³ |
| Secant modulus | | ASTMD882 | 235 Mpa |
| Secant modulus | | ASTMD882 | 281 Mpa |
| tensile strength | | ASTMD882 | 13.2 Mpa |
| tensile strength | | ASTMD882 | 14.7 Mpa |
| tensile strength | | ASTMD882 | 47.8 Mpa |
| tensile strength | | ASTMD882 | 42.3 Mpa |
| elongation | | ASTMD882 | 630 % |
| elongation | | ASTMD882 | 740 % |
| Falling hammer impact | | ASTMD1709A | 220 g |
| Elmondov tear strength | | ASTMD1922 | 250 g |
| Elmondov tear strength | | ASTMD1922 | 590 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D-1525 | 112 °C |
| Melting temperature | | Internal Method | 121 °C |
| vicat | | ASTMD1525 | 112 °C |
| | 内部方法 | 121 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.