Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 1110 | 0.12 % |
| density | | ISO 1183 | 1.85 g/cm³ |
| spiral flow length | | 内部方法 | 48.0 cm |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO 1172 | 60 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 23000 MPa |
| tensile strength | Break | ISO 527-2/5 | 210 MPa |
| Tensile strain | Break | ISO 527-2/5 | 1.5 % |
| Flexural modulus | | ISO 178 | 23600 MPa |
| bending strength | | ISO 178 | 325 MPa |
| Fracture bending strain | | ISO 178 | 1.7 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 50 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/C | 275 °C |
| melting temperature | | DIN EN11357-1 | 342 °C |
| Heat distortion temperature | | ISO 75-2/A | >280 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare