Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 2.0 % |
| density | | ISO 1183 | 1.42 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 2.4 g/10min |
| Shrinkage rate | | ISO 294-4 | 1.9 % |
| MediumDensity | | | 1.16 g/cm³ |
| SpecificHeatCapacity of Melt | | | 3000 J/kg/°C |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 94 |
| Rockwell hardness | R-Scale | ISO 2039-2 | 122 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | | FMVSS302 | B |
| burning rate | | ISO 3795 | 25 mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Emission | | VDA275 | <8.00 mg/kg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | | ISO 179/1eA | 9.5 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 11 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 340 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 3150 MPa |
| tensile strength | Yield | ISO 527-2 | 72.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 20 % |
| Nominal tensile fracture strain | | ISO 527-2 | 40 % |
| Flexural modulus | | ISO 178 | 2950 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 165 °C |
| Heat distortion temperature | | ISO 75-2/A | 98.0 °C |
| melting temperature | | ISO 11357-3 | 178 °C |
| AnnealingTemperature | | | 160 °C |
| AnnealingTime-Optional | | | 30.0 min/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.