PLA Ingeo™ 8052D NATUREWORKS USA
140
- Properties:Biodegradable
- Usages:filmFoambase tray
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 10 to 25 g/10 min | |
| Shrinkage rate | 0.30 - 0.50 % | ||
| melt mass-flow rate | ASTM D1238 | 14 g/10min | |
| Shrinkage rate | 0.30-0.50 % | ||
| relative viscosity | 内部方法 | 3.30 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Clarity | Transparent |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 48.3 Mpa | |
| elongation | ASTM D638 | 2.5 % | |
| Flexural modulus | ASTM D790 | 3830 Mpa | |
| bending strength | ASTM D790 | 82.7 Mpa | |
| tensile strength | ASTM D638 | 62.1 Mpa | |
| elongation | ASTM D638 | 3.5 % | |
| Flexural modulus | ASTM D790 | 3550 Mpa | |
| bending strength | ASTM D790 | 108 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Transition Temperature | ASTM D3417 | 55.0 to 65.0 °C | |
| Crystallization peak temperature | ASTM D3418 | 150 to 165 °C | |
| Glass Transition Temperature | ASTM D3418 | 55.0to65.0 °C | |
| Crystallization peak temperature | ASTM D3418 | 145to160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.