Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.29 g/cm³ |
| melt mass-flow rate | | ISO1133 | 10到18 g/10min |
| Shrinkage rate | | ISO294-4,ISO2577 | 1.0 % |
| Shrinkage rate | | ISO294-4,ISO2577 | 0.90 % |
| Water absorption rate | | ISO62 | 0.35 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/A | 68 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2270 MPa |
| Tensile stress | | ISO527-2 | 70.0 MPa |
| Tensile strain | Yield | ISO527-2 | 7.8 % |
| Flexural modulus | | ISO178 | 2400 MPa |
| Bending stress | | ISO178 | 105 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC60250 | 3.80 |
| dielectric constant | | IEC60250 | 3.70 |
| Dissipation Factor | | IEC60250 | 1.5E-03 |
| Dissipation Factor | | IEC60250 | 8.6E-03 |
| CTI | | IEC60112 | 150 V |
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 44 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ISO11357-2,DSC | 220 °C |
| | ISO11359-2 | 5.5E-05 cm/cm/°C |
| Heat distortion temperature | | ISO75-2/A | 196 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.