Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按重量计算的混合比:1.0 |
| | | 52 wk |
| | | 按重量计算的混合比:10 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Particle size | | | <20.0 µm |
| Ionic type | | | 47 ppm |
| Ionic type | | | 4 ppm |
| Ionic type | | | 4 ppm |
| Ionic type | | | 134 ppm |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| colour | | | Clear/Transparent |
| colour | | | Yellow |
| density | | | 0.988 g/cm³ |
| density | | | 1.20 g/cm³ |
| density | | | 4.2 Pa·s |
| density | | | >0.50 hr |
| density | Pot Life | | 480 min |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Supporting hardness | | | 88 |
| LapShearStrength | | | >13.8 MPa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | | 1.572 |
| transmissivity | | | >90.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| DegradationTemperature | | | 421 °C |
| Operating | | | -55到250 °C |
| Operating | | | -55到350 °C |
| Operating | | | 2.54 GPa |
| WeightLossonHeating | | | 0.33 % |
| WeightLossonHeating | | | 0.43 % |
| WeightLossonHeating | | | 0.74 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | 110 °C |
| | | 3.4E-05 cm/cm/°C |
| | | 1.3E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.