'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA6 8233GHS-BK-102 BASF GERMANY
163
Form：Granules | Grade：Injection grade
Properties:
Thermal stabilityhigh strengthOil resistant
Typical Applications:
HelmetAutomotive ApplicationsEngine parts
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | Helmet | Automotive Applications | Engine parts |
| Properties: | Thermal stability | high strength | Oil resistant |
Certificates
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 65 | kJ/m² |
| Dart impact | 23°C | Internal Method | 4.07 | J |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 3.0mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB | ||
| 0.60mm | UL 94 | HB | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | -40°C | ISO 527-2 | 10300 | Mpa |
| bending strength | 23°C | ASTM D790 | 280 | Mpa |
| 23°C | ISO 178 | 245 | Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 10200 | Mpa |
| 80°C | ISO 527-2 | 4820 | Mpa | |
| 120°C | ISO 527-2 | 4010 | Mpa | |
| 150°C | ISO 527-2 | 3560 | Mpa | |
| tensile strength | Break,-40°C | ASTM D638 | 230 | Mpa |
| Break,23°C | ASTM D638 | 180 | Mpa | |
| Break,80°C | ASTM D638 | 90.0 | Mpa | |
| Break,121°C | ASTM D638 | 70.0 | Mpa | |
| ASTM D638/ISO 527 | 125/18100 | kg/cm²(MPa)[Lb/in²] | ||
| Bending modulus | ASTM D790/ISO 178 | 5130/744000 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | Break,-40°C | ISO 527-2 | 230 | Mpa |
| Break,23°C | ISO 527-2 | 170 | Mpa | |
| Break,80°C | ISO 527-2 | 90.0 | Mpa | |
| Break,120°C | ISO 527-2 | 70.0 | Mpa | |
| Tensile strain | Break,23°C | ISO 527-2 | 3.0 | % |
| Bending modulus | 23°C | ASTM D790 | 8990 | Mpa |
| 23°C | ISO 178 | 8500 | Mpa | |
| tensile strength | Break,150°C | ISO 527-2 | 60.0 | Mpa |
| elongation | Break,-40°C | ASTM D638 | 3.0 | % |
| Break,23°C | ASTM D638 | 3.5 | % | |
| Break,80°C | ASTM D638 | 7.0 | % | |
| Break,121°C | ASTM D638 | 7.0 | % | |
| bending strength | ASTM D790/ISO 178 | 179/26000 | kg/cm²(MPa)[Lb/in²] | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| RTI Str | 3.0mm | UL 746 | 140 | °C |
| 1.5mm | UL 746 | 140 | °C | |
| 0.71mm | UL 746 | 130 | °C | |
| RTI Imp | 3.0mm | UL 746 | 120 | °C |
| 1.5mm | UL 746 | 115 | °C | |
| 0.71mm | UL 746 | 115 | °C | |
| Linear coefficient of thermal expansion | MD | ASTME831 | 3.8E-05 | cm/cm/°C |
| Melting temperature | ISO 3146 | 220 | °C | |
| ASTM D3418 | 220 | °C | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 205 | °C |
| 1.8MPa,Unannealed | ASTM D648 | 208 | °C | |
| RTI Elec | 3.0mm | UL 746 | 140 | °C |
| 1.5mm | UL 746 | 140 | °C | |
| 0.71mm | UL 746 | 130 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTM D648 | 218 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 215 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 1.8 | % |
| Equilibrium,50%RH | ASTM D570 | 1.8 | % | |
| Saturation,23°C | ISO 62 | 6.4 | % | |
| Saturation | ASTM D570 | 6.4 | % | |
| 23°C,24hr | ISO 62 | 1.1 | % | |
| 24hr | ASTM D570 | 1.1 | % | |
| Shrinkage rate | MD：3.18mm | 0.30 | % | |
| density | ASTM D792/ISO 1183 | 1.39 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Scale | ASTM D785 | 121 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.