ASA 796M BASF GERMANY

Form：Granules | Grade：Heat resistant grade

Properties:

High mobilityHigh impact resistance

Typical Applications:

Automotive ApplicationssheetApplication in the automotive field

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| sheet \| Application in the automotive field
Properties:	High mobility \| High impact resistance

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179	5.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	30	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/A	5.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/A	25	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	2000	Mpa
tensile strength	Yield,23°C	ISO 527-2	41.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2	3.5	%
bending strength		ISO 178	60.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
1.8MPa, annealed		ISO 75-2/A	95.0	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.0E-5到1.1E-4	cm/cm/°C
thermal conductivity		DIN 52612	0.17	W/m/K
0.45MPa, annealed		ISO 75-2/B	100	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.07	g/cm³
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	9.00	cm3/10min
Shrinkage rate		ISO 294-4	0.50-0.90	%
Water absorption rate	Saturation,23°C	ISO 62	1.7	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.35	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+13	ohms
Volume resistivity		IEC 60093	1E+14	ohms·cm
Dielectric constant	100Hz	IEC 60250	3.80
Dissipation factor	100Hz	IEC 60250	0.010
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.025
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	65.0	Mpa
film	Test Condition	Test Method	Test Result	Test Unit
elongation	Break		13	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.