ABS POLYLAC® PA-757 WH
562
- Properties:High glossHigh rigidityMedium impact resistance
- Usages:Home appliance componentsAutomotive sectorHousehold goods
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
| density | ISO 1183 | 1.04 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 30 g/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2/50 | 40.0 Mpa | |
| ISO 527-2/50 | 31.0 Mpa | ||
| Tensile strain | ISO 527-2/50 | 40 % | |
| Flexural modulus | ISO 178 | 2000 Mpa | |
| bending strength | ISO 178 | 61.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 29 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/1A | 27 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 83.0 °C | |
| ISO 75-2/A | 98.0 °C | ||
| vicat | ISO 306/A50 | 105 °C | |
| ISO 306/B50 | 101 °C | ||
| Linear coefficient of thermal expansion | ISO 11359-2 | 8.6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.