PA612 Zytel® 77G43L NC010 DUPONT USA

169

Properties:
Thermal stability
high strength
Usages:
Automotive components
Electronic and Electrical
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	横向流量	ISO 294-4	0.80	%
Shrinkage rate	Shrinkage rate	流量	ISO 294-4	0.30	%
Water absorption rate	饱和, 23°C, 2.00 mm	ISO 62	1.7	%
Water absorption rate	Water absorption rate	平衡, 23°C, 2.00 mm, 50% RH	ISO 62	0.70	%
Stickiness number		ISO 307	145	cm³/g

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R 计秤	ISO 2039-2	118
Tensile modulus		ISO 527-2	12500	Mpa
tensile strength	断裂	ISO 527-2	200	Mpa
elongation	断裂	ISO 527-2	3.0	%
Bending modulus		ISO 178	11000	Mpa
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	85	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100	kJ/m²

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45 MPa, 未退火	ISO 75-2/B	217	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, 未退火	ISO 75-2/A	203	°C
Glass transition temperature		ISO 11357-2	65.0	°C
Melting temperature		ISO 11357-3	218	°C
Linear coefficient of thermal expansion	流动	ISO 11359-2	1.4E-5	cm/cm/°C
	Linear coefficient of thermal expansion	流动 : -40 到 23°C	ISO 11359-2	2.1E-5	cm/cm/°C
		Linear coefficient of thermal expansion	流动 : 55 到 160°C	ISO 11359-2	1.3E-5	cm/cm/°C
			Linear coefficient of thermal expansion	横向	ISO 11359-2	1.1E-4	cm/cm/°C
				Linear coefficient of thermal expansion	横向 : -40 到 23°C	ISO 11359-2	7.5E-5	cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : 55 到 160°C	ISO 11359-2	1.4E-4	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC 62631-3-1	1.0E+13	ohms·m

Filling analysis	Test Condition	Test Method	Test Result	Unit
Top out temperature			210	°C

injection	Test Condition	Test Method	Test Result	Unit
drying temperature			80	°C
Drying time - hot air dryer			2.0 到 4.0	hr
Suggested maximum moisture content			0.20	%
Processing (melt) temperature			280 到 300	°C
Melt Temperature, Optimum			290	°C
Mold temperature			70 到 120	°C
Mold Temperature, Optimum			100	°C
Maintain pressure			50.0 到 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Maximum Screw Tangential Speed			12	m/min

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate	1.00 mm	ISO 3795	21	mm/min
UL flame retardant rating	0.71 mm	UL 94, IEC 60695-11-10, -20	HB
UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94, IEC 60695-11-10, -20	HB
FMVSS flammability		FMVSS 302	B
雾化 - G-value (condensate)		ISO 6452	1.0E-4	g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.